Physical Properties物理性質(zhì)

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Specific Gravity 密度

g/cc

 g/cc

ASTM D792

Maximum Moisture Content *水分含量

Injection Molding

Linear Mold Shrinkage, Flow 線性收縮率/流動(dòng)

cm/cm
@Thickness 3.20 mm

 in/in
@Thickness 0.126 in

ASTM D955

Melt Flow 熔體流動(dòng)速率

 g/10 min
@Load 2.16 kg,
Temperature 250 °C

 g/10 min
@Load 4.76 lb,
Temperature 482 °F

ASTM D1238

Mechanical Properties力學(xué)性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Tensile Strength, Yield 屈服拉伸強(qiáng)度

MPa
@Thickness 3.20 mm

psi
@Thickness 0.126 in

50mm/min; ASTM D638

Flexural Yield Strength 彎曲屈服強(qiáng)度

 MPa
@Thickness 3.20 mm

 psi
@Thickness 0.126 in

10mm/min; ASTM D790

Flexural Modulus 彎曲彈性模量

GPa
@Thickness 3.20 mm

 ksi
@Thickness 0.126 in

10mm/min; ASTM D790

Izod Impact, Notched 懸臂梁缺口沖擊強(qiáng)度

 J/cm
@Thickness 3.20 mm,
Temperature 23.0  °C

 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F

ASTM D256

Thermal Properties熱性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Deflection Temperature at熱變形溫度 0.46 MPa (66 psi) 

 °C
@Thickness 6.40 mm

 °F
@Thickness 0.252 in

Unannealed; ASTM D648

UL RTI, Electrical 相對(duì)溫度指數(shù)

 °C

 °F

UL RTI, Mechanical with Impact 機(jī)械沖擊熱指數(shù)

 °C

 °F

UL RTI, Mechanical without Impact 無(wú)機(jī)械沖擊熱指數(shù)

 °C