The perlite separates the heat preservation board (FSG hatred water heat preservation board) is take the inflated pearlite bulk as an aggregate, joins the water-repellent and the cementing agent carries on the heat insulation waterproofing heat preservation board which working procedures and so on configuration, screening, compression formation, drying make. The FSG hatred water heat preservation board has solved each kind of building roofing heat preservation, the heat insulation and the waterproof function effectively in a body's technical difficult problem, saved the massive constructions and the service fund.product characteristic:The nature is light, and heat preservation heat insulation performance fine fire protection. Dustproof. Moisture-proof, does not distort the modification, not rottenly mildewy, the non-toxic tasteless hatred water performance to be good, hates Shui Lvke to reach above 98% to construct safely easy and feasible, the roofing and the wall surface glue may the natural ore be raw materials, has the good environment-protective.

場(chǎng)上單一有機(jī)保溫材料易燃,存在安全隱患。無(wú)機(jī)材料保溫效果不理想。研制出高強(qiáng)輕質(zhì),防火保溫隔熱材料擁有廣闊市場(chǎng)空間。本實(shí)驗(yàn)采用水玻璃膠結(jié)經(jīng)硅氣凝膠浸泡后的膨脹珍珠巖顆粒,裝入模具熱壓制板。實(shí)驗(yàn)表明,板材抗壓強(qiáng)度為0.2MPa—0.3MPa,分析硅氣凝膠未能充分浸入膨脹珍珠巖顆粒。憎水性材料,分析經(jīng)硅氣凝膠改性導(dǎo)致板材憎水性能增強(qiáng)。導(dǎo)熱系數(shù)小可達(dá)0.049W·(m·k)-1,分析硅氣凝膠部分浸入顆粒內(nèi)部且充滿(mǎn)板材空隙,水玻璃密封效果較好。膨脹珍珠巖保溫板是集保溫、隔熱和防水功能于一體的新型外墻保溫板材。珍珠巖保溫板質(zhì)輕且保溫隔熱性能優(yōu)良,防火防塵防潮、不變形改性、不腐爛發(fā)霉、無(wú)毒無(wú)味憎水性能好(憎水率可達(dá)98%以上),施工安全簡(jiǎn)單易行,屋面與墻面粘貼均可以天然礦石為原料,有良好的環(huán)保性。但是珍珠巖在使用過(guò)程中會(huì)產(chǎn)生裂紋,產(chǎn)生裂紋

膨脹珍珠巖和陶粒兩種材料作為出色的保溫原材料,有著質(zhì)輕、隔熱、耐久、價(jià)廉的特點(diǎn),尤其是兩種材料的成分均為無(wú)機(jī)物,與傳統(tǒng)的聚苯乙烯泡沫塑料板等保溫材料相比又有著不凡的防火性能,所以在能源問(wèn)題日益嚴(yán)峻的背景下,越來(lái)越受到青睞,成為保溫工程中的重要原材料。其中,用膨脹珍珠巖和陶粒制成的輕集料混凝土保溫板材為常見(jiàn)的應(yīng)用方式。本論文將對(duì)以膨脹珍珠巖顆粒和陶粒顆粒作為主要原材料,并以陶砂代替普通砂來(lái)制作的節(jié)能保溫混凝土板材作以研究,探尋性能優(yōu)良的試驗(yàn)配合比及其制作工藝,同時(shí)得出其各項(xiàng)技術(shù)參數(shù),滿(mǎn)足作為建筑圍擋結(jié)構(gòu)的使用要求。主要的研究?jī)?nèi)容如下：(1)探討節(jié)能保溫混凝土的導(dǎo)熱理論和強(qiáng)度理論。確定以導(dǎo)熱系數(shù)為主要控制目標(biāo)來(lái)評(píng)定混凝土保溫功效的研究手段,與普通混凝土對(duì)比,闡述節(jié)能保溫混凝土的強(qiáng)度形成機(jī)制。(2)針對(duì)膨脹珍珠巖顆粒因吸水率偏高而難以大范圍推廣的問(wèn)題,特別采用憎水膨脹珍珠巖顆粒作為試驗(yàn)材料,大幅降低了膨脹珍珠巖混凝土的吸水率,為膨脹珍珠巖混凝土的進(jìn)一步應(yīng)用奠定了基礎(chǔ)。(3)詳細(xì)闡述節(jié)能保溫混凝土的制作工藝,分析制作過(guò)程中需要注意問(wèn)題,使其作為建筑保溫構(gòu)件的各種功能得以化發(fā)揮。

FSG憎水樹(shù)脂膨脹珍珠巖保溫板屋面保溫隔熱操作工藝1、工藝流程基層清理─→彈線找坡─→管根固定─→隔汽層鋪設(shè)─→抹找平層。2、操作步1）先將接觸面清掃干凈。2）按設(shè)計(jì)坡度及流水方向，找出屋面坡度走向，確定FSG憎水樹(shù)脂膨脹珍珠巖保溫板保溫層的厚度范圍。（3）穿越結(jié)構(gòu)層的管根在FSG憎水樹(shù)脂膨脹珍珠巖保溫板保溫層施工前，應(yīng)用細(xì)石砼塞堵密實(shí)。（4）FSG憎水樹(shù)脂膨脹珍珠巖保溫板應(yīng)緊靠在需保溫的基層表面上并應(yīng)鋪平墊穩(wěn)，分層鋪設(shè)的板材，其上、下兩層的接縫應(yīng)錯(cuò)開(kāi)，板之間用膠水貼嚴(yán)、粘牢，各層板間的縫隙，應(yīng)用同類(lèi)材料的碎屑嵌填密實(shí)，表面應(yīng)與相鄰兩板的高度一致排汽槽的留置應(yīng)與砂漿找平層分格縫一致，做找平層之前用寬約6cm的鍍鋅鐵皮覆蓋排汽道之上，以免水泥砂漿堵塞。